Wet chemical synthesis of Gd+3 doped vanadium Oxide/MXene based mesoporous hierarchical architectures as advanced supercapacitor material

In this paper, Gd³⁺ doped V₂O₅/Ti₃C₂T_x MXene (GVO/MX) hierarchical architectures have been synthesized by wet chemical approach. As prepared GVO/MX composite, along undoped VO and unsupported GVO were well characterized by XRD, FESEM, EDX, FT-IR and BET techniques. Electrochemical performance of VO, GVO and GVO/MX was evaluated by CV, GCD and EIS measurements. Among the three electrodes, GVO/MX composite exhibited highest electrochemical activity with the optimum specific capacitance of 1024 Fg^-1 at 10 mVs^?1. The specific capacitance of GVO/MX was ～1.7 and ～3 times higher than unsupported GVO (585 Fg^-1) and VO (326 Fg^-1), respectively. The cyclic life of GVO/MX with capacitance retention 96.12% was observed at 60 mVs^?1. EIS measurements showed reduction in electrochemical impedance for GVO/MX as compared to GVO and VO. The corresponding impedance values of Rct and Resr for GVO/MX were calculated as 18 Ω and 1.8 Ω, respectively. The superior capacitive ability of GVO/MX can be ascribed to its unique morphology, short diffusion path and high surface area of fabricated composite. Considering it, the present work provides a feasible strategy to fabricate highly effective electrode materials for next generation energy storage devices.     

The toughening design of multi-layer antioxidation coating on C/C matrix via SiC-SiCw transition layer grown in-situ

Poor antioxidant and thermal-shock capacities of C/C composites thermal barrier coating (TBC) caused by cracking and shedding of coatings has been a major obstacle blocking the development of C/C composites. Herein, in-situ growth of whisker reinforced silicon carbide transition layer and inter-embedding mechanism of multi-gradient coatings were brought into the design of TBC to enhance the antioxidant and thermal-shock capacities. A three-layer gradient coating SiC-SiC_w/ZrB₂-SiC/ZrSiO₄-aluminosilicate glass (ZAG) from inside to outside, in which ZrB₂-SiC/ZAG serve as oxygen barrier layers with self-healing ability and SiC-SiC_w provides thermal stress buffering and bonding against cracking and shedding of coatings, is designed. The ZAG mainly forms a dense oxygen blocking frontier with self-healing ability through fluidized glass, while the ZrB₂-SiC can react actively with infiltrated oxygen in a way of self-sacrifice, preventing oxygen erosion to C/C matrix and SiC-SiC_w transition layer. As a result, the collaborative work among layers endows this coating with excellent high temperature service performance. This work provides a new insight for the design of excellent TBC.     

Parameter estimation for a morphochemical reaction-diffusion model of electrochemical pattern formation

The process of electrodeposition can be described in terms of a reaction-diffusion partial differential equation (PDE) system that models the dynamics of the morphology profile and the chemical composition. Here we fit such a model to the different patterns present in a range of electrodeposited and electrochemically modified alloys using PDE constrained optimization. Experiments with simulated data show how the parameter space of the model can be divided into zones corresponding to the different physical patterns by examining the structure of an appropriate cost function. We then use real data to demonstrate how numerical optimization of the cost function can allow the model to fit the rich variety of patterns arising in experiments. The computational technique developed provides a potential tool for tuning experimental parameters to produce desired patterns.     

Preparation and luminescent properties of CaF2:Ln3+ (Ln:Er,Er/Yb)/Nafion composite films

In this work, CaF_2:Ln~(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray diffraction(XRD) and scanning electron microscopy(SEM). Composite films are transparent and CaF_2:Ln~(3+)(Ln:Er,Er/Yb) nanoparticles are well dispersed in Nafion films.The thicknesses of CaF_2:Er~(3+)/Nafion and CaF_2:Er~(3+),Yb~(3+)/Nafion composite film are about 77 and 73 μm,respectively. The nanoparticles in composite film possess cubic phase. CaF_2:Er~(3+),Yb~(3+)/Nafion composite film has stronger characteristic emission of Er~(3+) around 1530 nm with full width at half-maximum(FWHM) of 73 nm and longer luminescence lifetimes of 22.04 μs(25.03%) and 100.77 μs(74.97%).     

Formation mechanism of Ti(C,N) solid solution in Al-brown fused alumina refractory at 1973 K in flowing N2

Brown fused alumina is a cost-effective alumina material, and the state of Ti in alumina has a great influence on its high-temperature performance. In this paper, the Ti-containing phases in brown fused alumina particles and Al-brown fused alumina refractory were successfully transformed into Ti(C,N) at 1973 K in flowing N₂. The evolution of the Ti-containing phases in brown fused alumina under high temperature and nitrogen conditions was investigated by XRD, SEM and EDS. The results show that the Ti-containing phases in brown fused alumina include Ti₂O₃, Ti(C,N,O), TiFeSi₂, Ca_0·95Mg_0·9Al_10·1(Ti)O₁₇ and a low-melting point Ca₃Al₂Si₃(Mg,Ti)O₁₂ phase. Under high temperature and nitrogen conditions, the TiO_2[liquid], MgO_[liquid] and SiO_2[liquid] in the low-melting point phase are transformed into Ti(C,N), Mg(g) and SiO(g), while they are supplemented from Ti₂O₃, Ti(C,N,O) and Ca_0·95Mg_0·9Al_10·1(Ti)O₁₇. After heat treatment at 1973 K for 3 h, Ti₂O₃ and Ti(C,N,O) disappear, Ca_0·95Mg_0·9Al_10·1(Ti)O₁₇ is transformed into plate-like Ca_0·55Al₁₁O_17.05, and Ti(C,N) is formed on the surface of the corundum particles. The formation of Ti(C,N) reduces the porosity of the brown fused alumina particles and increases their strength.     

A comparative study on the catalytic activities and stabilities of atomic-layered platinum on dispersed Ti0.9Cu0.1N nanoparticles supported by N-doped carbon nanotubes (N-CNTs) and reduced graphene oxide (N-rGO)

In our previous research, titanium-based nitride with high conductivity and superior corrosion resistance were developed as an ideal core material for replacing noble metal to form Pt-based core-shell catalysts by pulse electrodeposition. Meanwhile, the smaller sizes of nitride cores would also be available for pulse electrodeposition by dispersing them on carbon nanotubes (CNT). To achieve a better practice on the preparation of the Pt-based core-shell catalysts, in this work, both nitrogen-doped carbon nanotubes (N-CNT) and reduced graphene oxide (N-rGO) were used to support the copper-doped titanium nitride (Ti_0.9Cu_0.1N) cores. In the course of pulse electrodeposition, their influences as supports on the electronic states of electrodeposited Pt as well as their catalytic activities were compared. The results showed that the Pt preferred to electrodeposit on Ti_0.9Cu_0.1N cores supported by N-CNT and formed a core-shell structure. While with the same electrodeposition process, the Pt was found to be electrodeposited not only on the Ti_0.9Cu_0.1N cores supported by N-rGO with heavy aggregations but also on the N-rGO support. Raman spectroscopy analysis indicated that the higher degree of structural defects on N-rGO, as support, might have contributed to such divergence observation.     

3D打印连续芳纶纤维/聚乳酸波纹夹层结构复合材料的压缩性能研究

以连续芳纶纤维(Kevlar)为增强体,热塑性聚乳酸(PLA)为基体,采用熔融沉积成型(FDM)工艺,设计并制备了一体成型的Kevlar/PLA波纹夹层结构复合材料。研究了Kevlar/PLA波纹夹层结构复合材料在压缩载荷下的断裂模式,分析了结构参数、工艺参数对试样的压缩性能和结构密度的影响。结果表明,随着芯层波纹数量的增加,试样的压缩性能与结构密度均呈增大趋势;随着芯层波纹高度的增大,试样的压缩强度先增大后减小,结构密度不断减小;随着打印层高的增大,试样中的纤维体积含量不断减少,试样的压缩强度略有下降。     

工艺参数对超声辅助脉冲电沉积镍-氮化钛复合镀层的影响

在45钢表面以超声波辅助脉冲电沉积制备Ni-TiN复合镀层。研究了平均阴极电流密度、脉冲占空比、超声功率和TiN粒子(平均直径20~30 nm)添加量对复合镀层的TiN粒子含量和显微硬度的影响。得到较优的工艺参数为:NiSO4ꞏ6H2O 300 g/L,NiCl2ꞏ6H2O 30 g/L,H3BO330 g/L,十二烷基硫酸钠0.3 g/L,TiN 25 g/L,pH 4.1~4.3,温度40°C,平均阴极电流密度4 A/dm2,脉冲占空比40%,脉冲频率1000 Hz,超声功率300 W,机械搅拌速率200 r/min,时间60 min。该条件下所得Ni-TiN复合镀层的TiN质量分数为8.35%,显微硬度为819 HV,表面平整、致密,晶粒尺寸均匀。     

Niobium and iron co-doped titania nanobelts for improving charge collection in dye-sensitized TiO2 solar cells

Niobium (Nb) and iron (Fe) co-doped titanium oxide nanobelts were prepared in a one-pot alkaline hydrothermal process followed by calcination treatment, and evaluated in TiO₂ nanoparticle-based composite anodes for dye-sensitized solar cells. Addition of Nb and Fe species caused an increase in donor density and trap-mediated charge transition, as characterized by electrochemical and photoluminescence analyses. Under illumination with simulated solar light, the co-doped single-crystalline nanobelts promoted photocurrent yield and open-circuit voltage, because they facilitate electronic conduction and chemical capacitance in the composite anodes. This improved photovoltaic performance is associated with the enhanced charge collection efficiency, mechanistically attributed to rapid electron transport and prolonged electron lifetime via shallow trapping sites. Results demonstrate that the Nb and Fe co-doped titania nanobelts are effective to provide longer electron diffusion lengths and favor charge accumulation during cell operation.